| Parameter |
Value |
|---|---|
|
Ultimate Tensile Strength |
12 MPa |
|
Tensile Modulus |
220 MPa |
|
Elongation |
13% |
|
Temp @ 5% Mass Loss |
249 ºC |
|
Ash Content (TGA) |
0.0 - 0.1% |
* Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from green parts, printed using Form 2, Castable 50 μm Fine Detail settings and washed without post-cure.
Washing
The foundational step in any SLA post-processing workflow is to remove any excess resin on the surface of the parts through an alcohol or ether wash.
Curing
Follow the recommended curing settings for the resin.
Form Cure V1 | Form Cure V2 | Form Cure L V1 | Form Cure L V2